Effect of Carbon Black Content on Curing Behavior of Polysulfide Coatings

Journal: Vol.11, No.2, Spring 2018 - Article 5   Pages :  103 Until 112

Article Code:

Z. Karami: University of Isfahan - Department of Chemical Engineering, Faculty of Engineering
O. Moini Jazani: University of Isfahan - Department of Chemical Engineering
A.H. Navarchian: University of Isfahan - Department of Chemical Engineering, Faculty of Engineering
M.R. Saeb: Institute for Color Science and Technology - Departments of Resin and Additives

Article's abstract:

Polysulfide is well known elastomer for use in aerospace applications due to providing flexible coating and chemically resistant sealants. In this work, the effects of carbon black content on curing behavior of polysulfide elastomer were investigated and Rheological properties for samples with different filler content 15, 20 and 25 phr were evaluated by rheometric mechanical spectrometer RMS. According to RMS analysis, sample with 20 phr carbon black had minimum gel point temperature and loss factor and highest elasticity. Also, the time sweep test for the optimal sample resulted from temperature and frequency sweep at 90°C was done and gel time obtained less than a few minutes. From the dynamic differential scanning calorimetry DSC diagram for polysulfide with 20 phr carbon black observed two exothermic peaks in heat flow for uncured sample. The first peak indicated the curing of polysulfide elastomer and second peak may be attributed the curing of resole resin and formation of methylene linkage.

Polysulfide elastomer, Carbon black, Rheological properties, Cure behavior

1. J. D. Zook, D.W. Jordan, D.M. Willard, G. Jones,M. Cosman, High strength polymers and aerospace sealants therefrom. 2002, Google Patents. 2. M.A. Cosman, Polymer blend and compositions and methods for using the same. 2009, Google Patents. 3. E.I. Zaitseva,A.A. Donskoi, Sealants based on polysulfide elastomers. Polym. Sci. Series D., 1(2008), 289-297. 4. J. Donaldson, S. Grimes, A. Houlson,S. Behn, Curing of a polysulfide sealant with sodium birnessite. J. Appl. Polym. Sci., 77(2000), 1177-1181. 5. M. Abdouss, T. Farajpour,M. Derakhshani, The effect of epoxy-polysulfide copolymer curing methods on mechanical-dynamical and morphological properties. Iran. J. Chem. Chem. Eng., 30(2011), 17-27. 6. B. Zhou, J. Zhang, Q. Wang,Q. Chen, Improvement in compression performance of the polysulfide sealant by thiol‐acrylate reaction. Polym. Eng. Sci., 52(2012), 912-919. 7. D. Vietti, M. Scherrer, Polymers Containing Sulfur, Polysulfides. Kirk-Othmer Encyclopedia of Chemical Technology, (2000). 8. M. R. Saeb, H. Vahabi, M. Jouyandeh, E. Movahedifar, R. Khalili, Epoxy-based flame retardant nanocomposite coatings: Comparison between functions of expandable graphene and halloysite nanotubes. Prog. Color, Colorants Coat., 10(2017), 245-252. 9. T. Matsui, M. Nakajima, T. Nonaka,N. Dokoshi, New liquid polysulfide polymer terminated with silyl group. J. Appl. Polym. Sci., 93(2004), 2642-2649. 10. A.V. Bray, D.D. Deppe, G. Schmidt, J.L. Massingill, P.N. Patel, C.E. Powell, and V.M. Mannari, Self-sealing fastener. 2014, Google Patents. 11. A. Usmani, Chemistry and technology of polysulfide sealants. Polym. Technol. Eng., 19(1982), 165-199. 12. R. Ramaswamy,P. S. Achary, Effect of curing agents on some properties of a polysulfide sealant. J. Appl. Polym. Sci., 30(1985), 3569-3578. 13. I. Novakov, A. Nistratov, M. Vaniev, V. Luk’yanichev,K.Y. Zershchikov, Effect of plasticizer nature on the cure rheokinetics and structure of Thiokol sealant vulcanizates. Polym. Sci. Series C., 49(2007), 71-73. 14. E. Zaitseva, A. Donskoi, V. Aleksashin,V. Evseeva, Properties of polysulfide sealants of VITEF type. Polym. Sci. Series C., 49(2007), 171-175. 15. J. Zhang, Z. Wang, G. Ding, Y. Quan,Q. Chen, The effect of epoxy resin to reduce the compression set of polysulfide sealant. J. Appl. Polym. Sci., 125(2012), 390-395. 16. Y.Y. Wang,J.Y. Meng. Effect of Thermo-Oxidative Ageing on Aviation Polysulfide Sealants. in Applied Mechanics and Materials. 2012. Trans Tech Publ. 17. H. Kasahara, K. Sako, T. Kosaka, H. Kudo, S. Takiyama,H. Kojo, Calcium carbonate filler for resin, process for producing the same, and resin composition containing the filler. 2015, Google Patents. 18. I. Rezaeian, P. Zahedi, A. Rezaeian, M. Ghadiri, F.M. Honarvar,A.H. Mohammadi, Optimized formulation of an oxidative curing system for liquid polysulfide sealants used in fuel tanks by D‐optimal design method. J. Appl. Polym. Sci., 120(2011), 2550-2562. 19. Y. Lu, J. Zhang, P. Chang, Y. Quan,Q. Chen, Effect of filler on the compression set, compression stress–strain behavior, and mechanical properties of polysulfide sealants. J. Appl. Polym. Sci., 120(2011), 2001-2007. 20. E. Zaitseva,A. Donskoi, Novel polysulfide sealing compositions for aircraft industry. Polym. Sci. Series D., 2(2009), 250-256. 21. E. Yarahmadi, K. Didehban, M. Shabanian,M.R. Saeb, High-performance starch-modified graphene oxide/epoxy nanocomposite coatings: A glimpse at cure kinetics and fracture behavior. Prog. Color Colorants Coat, 11(2018), 55-62. 22. L. Nachbaur, J. Mutin, A. Nonat,L. Choplin, Dynamic mode rheology of cement and tricalcium silicate pastes from mixing to setting. Cem. Concr. Res., 31(2001), 183-192. 23. J.-H. Lee, C.-M. Um,I.-b. Lee, Rheological properties of resin composites according to variations in monomer and filler composition. Dent Mater., 22(2006), 515-526. 24. H.A. Barnes, A handbook of elementary rheology. (2000). 25. R. Mafi, S. Mirabedini, M. Attar,S. Moradian, Cure characterization of epoxy and polyester clear powder coatings using Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Thermal Analysis (DMTA). Prog. Org. Coat., 54(2005), 164-169. 26. M.R. Kalaee, M.H.N. Famili,H. Mahdavi, Cure Kinetic of Poly (alkyltetrasulfide) Using a Rheological Method. Polym. Technol. Eng., 48(2009), 627-632. 27. B. Zhou, D. He, Y. Quan,Q. Chen, The investigation on the curing process of polysulfide sealant by in situ dielectric analysis. J. Appl. Polym. Sci., 126(2012), 1725-1732. 28. W. Wampler, B.M. Jacobsson, L. Nikiel, P.D. Cameron,J. Neilsen, Polysulfide treatment of carbon black filler and elastomeric compositions with polysulfide treated carbon black. 2015, Google Patents. 29. A. Harkous, G. Colomines, E. Leroy, P. Mousseau,R. Deterre, The kinetic behavior of Liquid Silicone Rubber: A comparison between thermal and rheological approaches based on gel point determination. React. Funct. Polym., 101(2016), 20-27. 30. H. Haddadi, E. Nazockdast,B. Ghalei, Chemorheological characterization of thermosetting polyurethane formulations containing different chain extender contents. Polym. Eng. Sci., 48(2008), 2446-2453. 31. M. Mravljak,M. Sernek, The influence of curing temperature on rheological properties of epoxy adhesives. Drvna Industrija, 62(2011), 19-25. 32. S.R. Raghavan, L.A. Chen, C. McDowell, S.A. Khan, R. Hwang,S. White, Rheological study of crosslinking and gelation in chlorobutyl elastomer systems. Polym., 37(1996), 5869-5875. 33. K. Prashantha, J. Soulestin, M.F. Lacrampe, P. Krawczak, G. Dupin,M. Claes, Masterbatch-based multi-walled carbon nanotube filled polypropylene nanocomposites: Assessment of rheological and mechanical properties. Compos. Sci. Technol., 69(2009), 1756-1763. 34. D. Dean, R. Walker, M. Theodore, E. Hampton,E. Nyairo, Chemorheology and properties of epoxy/layered silicate nanocomposites. Polym., 46(2005), 3014-3021. 35. B. Kiskan, B. Aydogan,Y. Yagci, Synthesis, characterization, and thermally activated curing of oligosiloxanes containing benzoxazine moieties in the main chain. J. Polym. Sci. Part A., 47(2009), 804-811. 36. W. Sichina, Characterization of epoxy resins using DSC. Thermal Analysis Application Note. Perkin Elmer Instruments, Norwalk, (2000). 37. X. Ramis, A. Cadenato, J. Morancho,J. Salla, Curing of a thermosetting powder coating by means of DMTA, TMA and DSC. Polym., 44(2003), 2067-2079. 38. J. McHugh,W. Stark, Determination and interpretation of changes in thermophysical properties of a carbon-fibre prepreg during cure. Polym. Test., 49(2016), 115-120. T. Sia, X. Liu, W.K. Chiu,R. Paton, Glass transition and viscoelastic behaviour of partially cured composites. Compos. Struct., 57(2002), 489-493

Article's file
Page view: 798
Article's download quantity : 21

Article System Login

Prof. Zahra Ranjbar
Dr. Farahnaz Nourmohammadian
Assistant Editor:
Dr. Mozhgan Hosseinnezhad
ISSN (online):
Institute for Color Science and Technology (ICST)

Quick Access
What is your opinion about the manuscript subscription system of PCCC website?
Website Statistics
Page view:799
Online Visitors:9